Repair filling Putty -

Putty used in conjunction with metallic objects, concrete and fibreglass to do repairs

FR179 - METAL FILLING PUTTY

Eli-Fil can be used in conjunction with any metallic object, e.g. to repair broken castings, tanks, parts of machinery, to level irregularities and fill blow holes to build up worn parts and to bond various metals, iron, steel, aluminium. It is also suitable for making tools, jigs, models, etc.

Mixing and Application

WORK TEMP

GEL TIME

CURE TIME

95ºC

45 - 60 min    @ 5mm

1½ – 2 hrs   @ 5mm

APPLICATION:

By spatula


VISCOSITY / 25°C:

Non-sagging paste


MIXING RATIO:

By weight:

100 parts of Resin "A"



25 parts of Hardener "B"


By Volume:

100 parts of Resin "A"



30 parts of Hardener "B"


Measurement:

Resin 1 x 12,5 ml spoon = 20g



Hardener 1 x 2 ml spoon= 5g

SPECIFIC GRAVITY / 25°C:

1.65 – 1.7 g/cm³


FR912 - METAL FILLING PUTTY

Eli-Fil FR912 Steel Putty can be used for emergency and permanent repairs of broken castings, tanks, parts of machinery, to level irregularities and fill blow holes, to build up worn parts and to bond various metals, ie. iron, steel aluminium. The product is also suitable for making tools, jigs, models, etc.

Mixing and Application

GEL TIME

CURE TIME

1½ - 1¾ Hours   @ 5mm

3 - 4 hrs @ 5mm

APPLICATION:

By spatula


VISCOSITY / 25°C:

Non-sagging paste


MIXING RATIO:

By weight:

100 parts of Resin



11 parts of Hardener


By Volume:

100 parts of Resin



35 parts of Hardener

COLOUR:

Metallic grey


SPECIFIC GRAVITY / 25°C:

1.65 – 1.7 g/cm³


WORK TEMP

120ºC

FR913 - METAL FILLING PUTTY

ENGINEERING / MINING  APPLICATIONS: The use of the FR/913 "quick set" Steel Putty is recommended where emergency repairs must be undertaken and time does not allow the application of the standard Eli-Fil range of Metal Filling Putties. Typical applications include repairs on damaged- leaking pipes, pumps, tanks and machine parts, to build up worn parts and linings in pumps, on impellers, shafts.


FOUNDRY APPLICATIONS: The paste like viscosity combined with excellent adhesion and strength on all ferrous and non-ferrous surfaces makes the steel putty an ideal product to fill blow holes, incorrectly drilled holes and surface blemishes in ferrous and non-ferrous castings and patterns.

Mixing and Application

GEL TIME

CURE TIME

3 min @ 5mm

6 min @ 5mm

APPLICATION:

By spatula


VISCOSITY / 25°C:

Paste


MIXING RATIO:

By weight:

100 parts of Resin



21-22 Parts of Hardener


By Volume:

100 parts of Resin



55-58 Parts of Hardener

COLOUR:

Metallic grey


SPECIFIC GRAVITY / 25°C:

2.9 – 2.95 g/cm3


WORK TEMP

100ºC

FR955 - ALUMINIUM PUTTY

An ambient temperature curing, two component Epoxy Putty formulated with an Aluminium Filler.

Mixing and Application

GEL TIME

CURE TIME

2½ – 3 hrs @ 5mm

24 Hours

APPLICATION:

By spatula


VISCOSITY / 25°C:

Paste


MIXING RATIO:

By weight:

100 parts of Resin



10-11 Parts of Hardener


By Volume:

12,5 ml spoon = 23.5g Resin



2 ml spoon = 2.5 g Hardener

COLOUR:

Metallic grey


SPECIFIC GRAVITY / 25°C:

1.9 – 2.0 g/cm3


WORK TEMP

120ºC

WORK TIME

50 min

FR983 - ABRASION RESISTANT PUTTY

An ambient temperature curing, two component Epoxy Putty formulated with an Aluminium Filler.

Mixing and Application

GEL TIME

CURE TIME

20 min @ 5mm

35 min @ 5mm

APPLICATION:

By spatula


VISCOSITY / 25°C:

Thixotropic Paste


MIXING RATIO:

By weight:

100 parts of Resin



9 Parts of Hardener


By Volume:

100 Parts of Resin



19 - 20 Parts of Hardener

COLOUR:

Metallic grey


SPECIFIC GRAVITY / 25°C:

2.4 – 2.5 g/cm3


WORK TEMP

100ºC

WORK TIME

15 min

FR308 - METAL FILLING PUTTY

High performance non sagging epoxy putty that sets rock hard. Once cured the repaired area can be machined, drilled and tapped. Available in Black or White. Once cured it can be painted.

Mixing and Application

GEL TIME

CURE TIME

1 – 1½ hrs

2 – 2½ hrs

APPLICATION:

By hand, spatula, knife


VISCOSITY / 25°C:

Non-sagging putty


MIXING RATIO:

By weight:

1 Part Resin



1 Part Hardener


By Volume:

1 Part Resin



1 Part Hardener

COLOUR:

Black or White


SPECIFIC GRAVITY / 25°C:

2.4 – 2.5 g/cm3


WORK TEMP

90ºC

FR986A - MARINE PUTTY/WET SURFACE REPAIR PUTTY

The Eli-Fil FR/986 marine putty can be applied under adverse cold environmental conditions to damp - wet surfaces, e.g. concrete, rock, metal, etc.

Eli-Fil FR/986 is a filler and fibreglass reinforced two component Epoxy Repair Putty.

Mixing and Application

GEL TIME

CURE TIME UNDER WATER

1 hour

5 hrs

APPLICATION:

By spatula


VISCOSITY / 25°C:

Thixotropic Paste


MIXING RATIO:

By weight:

1 Part Resin



1 Part Hardener


By Volume:

1 Part Resin



1 Part Hardener

COLOUR:

White


COVERAGE:

1kg pack covers 0,35m2 - 0,55 m2

CURE TIME ABOVE WATER

3 - 3½ hrs

epoxy A5 booklet.pdf